Synthesis of multivalent silica nanoparticles combining both enthalpic and entropic patchiness

Résumé

Silica particles with a controlled number of entropic patches, i.e. dimples, are synthesized through the growth of the silica core of binary multipods that have been produced by a seeded-growth emulsion polymerization reaction. Transmission electron microscopy studies indicate that the silica surface conforms to the shape of the polystyrene (PS) nodules of the multipods while growing, allowing good control of the final shape of the dimpled silica particles. The PS nodules are also used as protecting masks to regioselectively graft amino groups, as revealed by the adsorption of gold markers. After dissolution of the PS nodules, some polymer chains remain grafted onto the silica surface, forming organic bumps. These residues are also selectively functionalized, leading to silica particles with both entropic and enthalpic patches.

Domaines

Matériaux
Fichier principal
Vignette du fichier
2015-119.pdf (1.63 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01187264 , version 1 (25-02-2021)

Identifiants

Citer

Céline Hubert, Cyril Chomette, Anthony Désert, Ming Sun, Mona Tréguer-Delapierre, et al.. Synthesis of multivalent silica nanoparticles combining both enthalpic and entropic patchiness. Faraday Discussions, 2015, 181, pp.139-146. ⟨10.1039/c4fd00241e⟩. ⟨hal-01187264⟩
175 Consultations
97 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More